Thermoplastic polymer blends of isotactic polypropylene and alpha-olefin/propylene copolymers

ABSTRACT

Improved thermoplastic polymer blend compositions comprising an isotactic polypropylene component and an alpha-olefin and propylene copolymer component, said copolymer comprising crystallizable alpha-olefin sequences. In a preferred embodiment, improved thermoplastic polymer blends are provided comprising from about 35% to about 85% isotactic polypropylene and from about 30% to about 70% of an ethylene and propylene copolymer, wherein said copolymer comprises isotactically crystallizable propylene sequences and is predominately propylene. The resultant blends manifest unexpected compatibility characteristics, increased tensile strength, and improved process characteristics, e.g., a single melting point.

This application is a continuation of Ser. No. 10/613,373, filed Jul. 3, 2003 pending which is a continuation of Ser. No. 08/910,001, filed Aug. 12, 1997, now U.S. Pat. No. 6,635,715, the disclosures of which are incorporated by reference in their entireties.

FIELD OF THE INVENTION

The invention relates to polymer blends of at least two polymers having surprising properties when compared to the properties of the individual polymers prior to blending. More specifically, the invention relates to blends of thermoplastic polymers, e.g., according to one embodiment, isotactic polypropylene and an olefin copolymer. The invention further relates to thermoplastic polymer blends comprising isotactic polypropylene and, according to one embodiment, a copolymer of ethylene and propylene, wherein the copolymer comprises isotactically crystallizable alpha-olefin sequences. In addition, the invention relates to methods for making the above polymers and blends thereof.

BACKGROUND OF THE INVENTION

Although blends of isotactic polypropylene and ethylene propylene rubber are well known in the prior art, prior art Ziegler-Natta catalyst systems could only produce ethylene propylene rubber compositions with greater than 30% by weight ethylene at practical, economic polymerization conditions. There exists a need for polymeric materials which have advantageous processing characteristics while still providing suitable end properties to articles formed therefrom, e.g., tensile and impact strength. Copolymers and blends of polymers have been developed to try and meet the above needs. U.S. Pat. No. 3,882,197 to Fritz et al. describes blends of stereoregular propylene/alpha-olefin copolymers, stereoregular propylene, and ethylene copolymer rubbers. In U.S. Pat. No. 3,888,949 Chi-Kai Shih, assigned to E I DuPont, shows the synthesis of blend compositions containing isotactic polypropylene and copolymers of propylene and an alpha-olefin, containing between 6–20 carbon atoms, which have improved elongation and tensile strength over either the copolymer or isotactic polypropylene. Copolymers of propylene and alpha-olefin are described wherein the alpha-olefin is hexene, octene or dodecene. However, the copolymer is made with a heterogeneous titanium catalyst which makes copolymers which are non-uniform in compositional distribution and typically broad in molecular weight distribution. Compositional distribution is a property of copolymers where there exists statistically significant intermolecular or intramolecular difference in the composition of the polymer. Methods for measuring compositional distribution are described later. The presence of intramolecular compositional distribution is described in U.S. Pat. No. 3,888,949 by the use of the term “block” in the description of the polymer where the copolymer is described as having “sequences of different alpha-olefin content.” Within the context of the invention described above the term sequences describes a number of olefin monomer residues catenated together by chemical bonds and obtained by a polymerization procedure.

In U.S. Pat. No. 4,461,872, A.C.L. Su improved on the properties of the blends described in U.S. Pat. No. 3,888,949 by using another heterogeneous catalyst system. However, the properties and compositions of the copolymer with respect to either the nature and type of monomers (alpha-olefin containing 6–20 carbon atoms) or the blocky heterogeneous intra/inter molecular distribution of the alpha-olefin in the polymer have not been resolved since the catalysts used for these polymerization of propylene and alpha-olefin are expected to form copolymers which have statistically significant intermolecular and intramolecular compositional differences.

In two successive publications in the journal of Macromolecules, 1989, V22, pages 3851–3866, J. W. Collette of E. I. DuPont has described blends of isotactic polypropylene and partially atactic polypropylene which have desirable tensile elongation properties. However, the partially atactic propylene has a broad molecular weight distribution as shown in FIG. 8 of the first publication. The partially atactic polypropylene is also composed of several fractions, which differ in the level of tacticity of the propylene units as shown by the differences in the solubility in different solvents. This is shown by the corresponding physical decomposition of the blend which is separated by extraction with different solvents to yield individual components of uniform solubility characteristics as shown in Table IV of the above publications.

In U.S. Pat. Nos. 3,853,969 and 3,378,606, E. G. Kontos discloses the formation of in situ blends of isotactic polypropylene and “stereo block” copolymers of propylene and another olefin of 2 to 12 carbon atoms, including ethylene and hexene. The copolymers of this invention are necessarily heterogeneous in intermolecular and intramolecular composition distribution. This is demonstrated by the synthesis procedures of these copolymers which involve sequential injection of monomer mixtures of different compositions to synthesize polymeric portions of analogously different compositions. In addition, FIG. 1 of both patents shows that the “stereo block” character, which is intra or intermolecular compositional differences in the context of the description of the present invention, is essential to the benefit of the tensile and elongation properties of the blend. In situ blends of isotactic polypropylene and compositionally uniform random ethylene propylene copolymers have poor properties. Moreover, all of these compositions either do not meet all of the desired properties for various applications, and/or involve costly and burdensome process steps to achieve the desired results.

Similar results are anticipated by R. Holzer and K. Mehnert in U.S. Pat. No. 3,262,992 assigned to Hercules wherein the authors disclose that the addition of a stereoblock copolymer of ethylene and propylene to isotactic polypropylene leads to improved mechanical properties of the blend compared to isotactic polypropylene alone. However, these benefits are described only for the stereoblock copolymers of ethylene and propylene. The synthesis of the these copolymers is designed around polymerization conditions where the polymer chains are generated in different compositions of ethylene and propylene achieved by changing, with time, the monomer concentrations in the reactor. This is shown in examples 1 and 2. The stereoblock character of the polymer is graphically shown in the molecular description (column 2, line 65) and contrasted with the undesirable random copolymer (column 2, line 60). The presence of stereoblock character in these polymers is shown by the high melting point of these polymers, which is much greater than the melting point of the second polymer component in the present invention, shown in Table 1, as well as the poor solubility of these hetero block materials, as a function of the ethylene wt % of the material as shown in Table 3.

It would be desirable to produce a blend of a crystalline polymer, hereinafter referred to as the “first polymer component,” and a crystallizable polymer, hereinafter referred to as the “second polymer component”, having advantageous processing characteristics while still providing end products made from the blend composition having the desired properties, i.e., increased tensile strength, elongation, and overall toughness. The first polymer component (abbreviated as “FPC” in the Tables below) and the second polymer component (abbreviated as “SPC” in the Tables below). Indeed, there is a need for an entirely polyolefin composition which is thermally stable, heat resistant, light resistant and generally suitable for thermoplastic elastomer (TPE) applications which has advantageous processing characteristics. Such an entirely polyolefin composition would be most beneficial if the combination of the first polymer component and the second polymer component were significantly different in mechanical properties than the compositionally weighted average of the corresponding properties of first polymer component and second polymer component alone. We anticipate, while not meant to be limited thereby, that the potency of the second polymer component may be increased if it only consists of one or two polyolefin copolymers material defined by uniform intramolecular and intermolecular composition and microstructure.

The term “crystalline,” as used herein for first polymer component, characterizes those polymers which possess high degrees of inter- and intra-molecular order, and which melt higher than 110° C. and preferably higher than 115° C. and have a heat of fusion of at least 75 J/g, as determined by DSC analysis. And, the term “crystallizable,” as used herein for second polymer component, describes those polymers or sequences which are mainly amorphous in the undeformed state, but upon stretching or annealing, crystallization occurs. Crystallization may also occur in the presence of the crystalline polymer such as first polymer component. These polymers have a melting point of less than 105° C. or preferably less than 100° C. and a heat of fusion of less than 75 J/g as determined by DSC.

SUMMARY OF THE INVENTION

The present invention, according to one embodiment, is directed to the use of chiral metallocene catalysts to (1) readily produce second polymer component being ethylene propylene rubber compositions with about 4 wt % to about 25 wt % ethylene, and (2) readily produce second polymer component compositions containing isotactic propylene sequences long enough to crystallize. Thus, the invention is directed, according to one embodiment, to semicrystalline materials (second polymer component), which when blended with isotactic polymers (first polymer component), show an increased level of compatibility between the ethylene propylene and isotactic polypropylene phases. While not meant to be limited thereby, we believe the increased compatibility is due to the similarity of the composition of the first polymer component and all of the second polymer component. Thus, the uniformity of the intra- and inter-molecular composition of the second polymer component is of importance. In particular, it is important that substantially all of the components of the second polymer component be within the narrow composition range of ethylene and propylene defined above. In addition, the presence of isotactic propylene sequences in the second polymer component is of benefit for the improved adhesion of the domains of the first polymer component and the second polymer component in the polymer blend composition. As a result, blends of isotactic polypropylene with ethylene propylene copolymers according to the invention, have improved physical properties as compared to isotactic polypropylene blends with prior art ethylene propylene rubbers.

According to one embodiment, a composition of the present invention comprises a blend of at least a first polymer component and a second polymer component. The blend comprises greater than about 2% by weight of the first polymer component comprising an alpha-olefin propylene copolymer containing isotactic polypropylene crystallinity with a melting point of about 115° C. to about 170° C. The blend also contains a second polymer component comprising a copolymer of propylene and at least one other alpha-olefin having less than 6 carbon atoms, and preferably 2 carbon atoms. The second polymer component copolymer of the invention, according to one embodiment, comprises isotactically crystallizable propylene sequences and greater than 75% by weight propylene and preferably greater than 80% by weight propylene.

According to another embodiment, a thermoplastic polymer blend composition of the invention comprises a first polymer component and a second polymer component. The first polymer component comprises isotactic polypropylene, and is present in an amount of about 2% to about 95% by weight and more preferably 2% to 70% by weight of the total weight of the blend. The first polymer component may also be comprised of commonly available isotactic polypropylene compositions referred to as impact copolymer or reactor copolymer. However these variations in the identity of the first polymer component are acceptable in the blend only to the extent that all of the components of the first polymer component are substantially similar in composition and the first polymer component is within the limitations of the crystallinity and melting point indicated above. This first polymer component may also contain additives such as flow improvers, nucleators and antioxidants which are normally added to isotactic polypropylene to improve or retain properties. All of these polymers are referred to as the first polymer component.

The second polymer component is a thermoplastic comprising a random copolymer of ethylene and propylene having a melting point by DSC of 25° C. to 105° C., preferably in the range 25° C. to 90° C., more preferably in the range of 40° C. to 90° C. and an average propylene content by weight of at least 75% and more preferably at least 80%. The second polymer component is made with a polymerization catalyst which forms essentially or substantially isotactic polypropylene, when all or substantially all propylene sequences in the second polymer component are arranged isotactically. This copolymer contains crystallizable propylene sequences due to the isotactic polypropylene. The second polymer component is statistically random in the distribution of the ethylene and propylene residues along the chain. Quantitative evaluation of the randomness of the distribution of the ethylene and propylene sequences may be obtained by consideration of the experimentally determined reactivity ratios of the second polymer component. We believe that the second polymer component is random in the distribution of ethylene and propylene sequences since (1) it is made with a single sited metallocene catalyst which allows only a single statistical mode of addition of ethylene and propylene and (2) it is made in a well mixed, continuous monomer feed stirred tank polymerization reactor which allows only a single polymerization environment for substantially all of the polymer chains of the second polymer component. Thus there is substantially no statistically significant difference in the composition of the second polymer component either among two polymer chains or along any one chain.

The ratio of the first polymer component to the second polymer component of the blend composition of the present invention may vary in the range of 2:98 to 95:5 by weight and more preferably in the range 2:98 to 70:30 by weight.

According to another embodiment of the present invention, the second polymer component may contain small quantities of a non-conjugated diene to aid in the vulcanization and other chemical modification of the blend of the first polymer component and the second polymer component. The amount of diene is limited to be no greater than 10 wt % and preferably no greater than 5 wt %. The diene may be selected from the group consisting of those which are used for the vulcanization of ethylene propylene rubbers and preferably ethyldiene norbornene, vinyl norbornene and dicyclopentadiene.

According to still a further embodiment, the invention is directed to a process for preparing thermoplastic polymer blend compositions. The process comprises: (a) polymerizing propylene or a mixture of propylene and one or more monomers selected from C₂ or C_(4–C) ₁₀ alpha olefins in the presence of a polymerization catalyst wherein a substantially isotactic propylene polymer containing at least about 90% by weight polymerized propylene is obtained; (b) polymerizing a mixture of ethylene and propylene in the presence of a chiral metallocene catalyst, wherein a copolymer of ethylene and propylene is obtained comprising up to about 25% by weight ethylene and preferably up to 20% by weight ethylene and containing isotactically crystallizable propylene sequences; and (c) blending the propylene polymer of step (a) with the copolymer of step (b) to form a blend.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

The blend compositions of the present invention generally are comprised of two components: (1) a first polymer component comprising isotactic polypropylene, and (2) a second polymer component comprising an alpha-olefin (other than propylene) and propylene copolymer.

The First Polymer Component (FPC)

In accordance with the present invention, the first thermoplastic polymer component (first polymer component), i.e., the polypropylene polymer component may be homopolypropylene, or copolymers of propylene, or some blends thereof. The polypropylene used in the present blends can vary widely in form. For example, substantially isotactic polypropylene homopolymer can be used or the polypropylene can be in the form of a copolymer containing equal to or less than about 10 weight percent of other monomer, i.e., at least about 90% by weight propylene. Further, the polypropylene can be present in the form of a graft or block copolymer, in which the blocks of polypropylene have substantially the same stereoregularity as the propylene-alpha-olefin copolymer, so long as the graft or block copolymer has a sharp melting point above about 110° C. and preferably above 115° C. and more preferably above 130° C., characteristic of the stereoregular propylene sequences. The first polymer component of the present invention is predominately crystalline, i.e., it has a melting point generally greater than about 110° C., preferably greater than about 115° C., and most preferably greater than about 130° C. The propylene polymer component may be a combination of homopolypropylene, and/or random, and/or block copolymers as described herein. When the above propylene polymer component is a random copolymer, the percentage of the copolymerized alpha-olefin in the copolymer is, in general, up to about 9% by weight, preferably about 2% to about 8% by weight, most preferably about 2% to about 6% by weight. The preferred alpha-olefins contain 2 or from 4 to about 12 carbon atoms. The most preferred alpha-olefin is ethylene. One, or two or more alpha-olefins can be copolymerized with propylene.

Exemplary alpha-olefins may be selected from the group consisting of ethylene; butene-1; pentene-1,2-methylpentene-1,3-methylbutene-1; hexene-1,3-methylpentene-1,4-methylpentene-1,3,3-dimethylbutene-1; heptene-1; hexene-1; methylhexene-1; dimethylpentene-1 trimethylbutene-1; ethylpentene-1; octene-1; methylpentene-1; dimethylhexene-1; trimethylpentene-1; ethylhexene-1; methylethylpentene-1; diethylbutene-1; propylpentane-1; decene-1; methylnonene-1; nonene-1; dimethyloctene-1; trimethylheptene-1; ethyloctene-1; methylethylbutene-1; diethylhexene-1; dodecene-1 and hexadodecene-1.

The thermoplastic polymer blend compositions of the present invention may comprise from about 2% to about 95% by weight of first polymer component. According to a preferred embodiment, the thermoplastic polymer blend composition of the present invention may comprise from about 2% to about 70% by weight of the first polymer component. According to the most preferred embodiment, the compositions of the present invention may comprise from about 5% to about 70% by weight of the first polymer component.

There is no particular limitation on the method for preparing this propylene polymer component of the invention. However, in general, the polymer is a propylene homopolymer obtained by homopolymerization of propylene in a single stage or multiple stage reactor. Copolymers may be obtained by copolymerizing propylene and an alpha-olefin having 2 or from 4 to about 20 carbon atoms, preferably ethylene, in a single stage or multiple stage reactor. Polymerization methods include high pressure, slurry, gas, bulk, or solution phase, or a combination thereof, using a traditional Ziegler-Natta catalyst or a single-site, metallocene catalyst system. The catalyst used is preferably one which has a high isospecificity. Polymerization may be carried out by a continuous or batch process and may include use of chain transfer agents, scavengers, or other such additives as deemed applicable.

The Second Polymer Component (SPC)

The second polymer component of the polymer blend compositions of the present invention comprises a copolymer of propylene and another alpha-olefin having less than 6 carbon atoms, preferably ethylene. Optionally, the second component of the composition of the present invention may further comprise, in addition to the above mentioned, amounts of a diene. The second polymer component of the present inventive composition preferably, according to one embodiment, comprises a random copolymer having a narrow compositional distribution. While not meant to be limited thereby, it is believed that the narrow composition distribution of the second polymer component is important. The intermolecular composition distribution of the polymer is determined by thermal fractionation in a solvent. A typical solvent is a saturated hydrocarbon such as hexane or heptane. This thermal fractionation procedure is described below. Typically, approximately 75% by weight and more preferably 85% by weight of the polymer is isolated as a one or two adjacent, soluble fraction with the balance of the polymer in immediately preceding or succeeding fractions. Each of these fractions has a composition (wt % ethylene content) with a difference of no greater than 20 wt. % (relative) and more preferably 10 wt % (relative) of the average wt % ethylene content of the whole second polymer component. The second polymer component is narrow in compositional distribution if it meets the fractionation test outlined above.

In all second polymer component, the number and distribution of ethylene residues is consistent with the random statistical polymerization of ethylene, propylene and optional amounts of diene. In stereoblock structures, the number of monomer residues of any one kind adjacent to one another is greater than predicted from a statistical distribution in random copolymers with a similar composition. Historical polymers with stereoblock structure have a distribution of ethylene residues consistent with these blocky structures rather than a random statistical distribution of the monomer residues in the polymer. The intramolecular composition distribution of the polymer may be determined by C-13 NMR which locates the ethylene residues in relation to the neighboring propylene residue. A more practical and consistent evaluation of the randomness of the distribution of the ethylene and propylene sequences may be obtained by the following consideration. We believe that the second polymer component is random in the distribution of ethylene and propylene sequences since (1) it is made with a single sited metallocene catalyst which allows only a single statistical mode of addition of ethylene and propylene and (2) it is made in a well mixed, continuous monomer feed stirred tank polymerization reactor which allows only a single polymerization environment for substantially all of the polymer chains of the second polymer component.

The second polymer component preferably, according to one embodiment of the invention, has a single melting point. The melting point is determined by DSC. Generally, the copolymer second component of the present invention has a melting point below the first polymer component of the blend typically between about 105° C. and 25° C. Preferably, the melting point of second polymer component is between about 90° C. and 25° C. Most preferably, according to one embodiment of the present invention, the melting point of the second polymer component of the composition of the present invention is between 90° C. and 40° C.

The second polymer component preferably has a narrow molecular weight distribution (MWD) between about 1.8 to about 5.0, with a MWD between about 2.0 to about 3.2 preferred.

The second polymer component of the present inventive composition comprises isotactically crystallizable alpha-olefin sequences, e.g., preferably propylene sequences (NMR). The crystallinity of the second polymer component is, preferably, according to one embodiment, from about 2% to about 65% of homoisotactic polypropylene, preferably between 5% to 40%, as measured by the heat of fusion of annealed samples of the polymer.

According to another embodiment of the present invention, the second polymer component of the composition comprises from about 5% to about 25% by weight alpha-olefin, preferably from about 6% to about 20% by weight alpha-olefin, and most preferably, it comprises from about 6% to about 18% by weight alpha-olefin and even more preferably between 10% to 16% by alpha-olefin. These composition ranges for the second polymer component are dictated by the object of the present invention. At alpha-olefin compositions lower than the above lower limits for the second polymer component, the blends of the first polymer component and second polymer component are hard and do not have the favorable elongation properties of the blends of the present invention. At alpha-olefin compositions higher than the above higher limits for the second polymer component, the blends of the second polymer component and the first polymer component do not have the favorable tensile properties of the blends of the present invention. It is believed, while not meant to be limited thereby, the second polymer component needs to have the optimum amount of isotactic polypropylene crystallinity to crystallize with the first polymer component for the beneficial effects of the present invention. As discussed above, the preferred alpha-olefin is ethylene.

The compositions of the present invention may comprise from about 5% to about 98% by weight of the second polymer component. According to one preferred embodiment, the compositions of the present invention may comprise from about 30% to about 98% by weight of the second polymer component. Most preferably, the compositions of the present invention comprise from about 30% to about 95% by weight of the second polymer component.

Generally, without limiting in any way the scope of the invention, one means for carrying out a process of the present invention for the production of the copolymer second polymer component is as follows: (1) liquid propylene is introduced in a stirred-tank reactor, (2) the catalyst system is introduced via nozzles in either the vapor or liquid phase, (3) feed ethylene gas is introduced either into the vapor phase of the reactor, or sparged into the liquid phase as is well known in the art, (4) the reactor contains a liquid phase composed substantially of propylene, together with dissolved alpha-olefin, preferably ethylene, and a vapor phase containing vapors of all monomers, (5) the reactor temperature and pressure may be controlled via reflux of vaporizing propylene (autorefrigeration), as well as by cooling coils, jackets, etc., (6) the polymerization rate is controlled by the concentration of catalyst, temperature, and (7) the ethylene (or other alpha-olefin) content of the polymer product is determined by the ratio of ethylene to propylene in the reactor, which is controlled by manipulating the relative feed rates of these components to the reactor.

For example, a typical polymerization process consists of a polymerization in the presence of a catalyst comprising a bis (cyclopentadienyl) metal compound and either 1) a non-coordinating compatible anion activator, or 2) an alumoxane activator. According to one embodiment of the invention, this comprises the steps of contacting ethylene and propylene with a catalyst in a suitable polymerization diluent, said catalyst comprising, for example, according to a preferred embodiment, a chiral metallocene catalyst, e.g., a bis (cyclopentadienyl) metal compound, as described in U.S. Pat. No. 5,198,401 which is herein incorporated by reference for purposes of U.S. practices and an activator. The activator used may be an alumoxane activator or a non-coordination compatible anion activator. The alumoxane activator is preferably utilized in an amount to provide a molar aluminum to metallocene ratio of from about 1:1 to about 20,000:1 or more. The non-coordinating compatible anion activator is preferably utilized in an amount to provide a molar ratio of biscyclopentadienyl metal compound to non-coordinating anion of 10:1 to about 1:1. The above polymerization reaction is conducted by reacting such monomers in the presence of such catalyst system at a temperature of from about −100° C. to about 300° C. for a time of from about 1 second to about 10 hours to produce a copolymer having a weight average molecular weight of from about 5,000 or less to about 1,000,000 or more and a molecular weight distribution of from about 1.8 to about 4.5.

While the process of the present invention includes utilizing a catalyst system in the liquid phase (slurry, solution, suspension or bulk phase or combination thereof), according to other embodiments, high pressure fluid phase or gas phase polymerization can also be utilized. When utilized in a gas phase, slurry phase or suspension phase polymerization, the catalyst systems will preferably be supported catalyst systems. See, for example, U.S. Pat. No. 5,057,475 which is incorporated herein by reference for purposes of U.S. practice. Such catalyst systems can also include other well known additives such as, for example, scavengers. See, for example, U.S. Pat. No. 5,153,157 which is incorporated herein by reference for purposes of U.S. practices. These processes may be employed without limitation of the type of reaction vessels and the mode of conducting the polymerization. As stated above, and while it is also true for systems utilizing a supported catalyst system, the liquid phase process comprises the steps of contacting ethylene and propylene with the catalyst system in a suitable polymerization diluent and reacting the monomers in the presence of the catalyst system for a time and at a temperature sufficient to produce an ethylene-propylene copolymer of the desired molecular weight and composition.

It is understood in the context of the present invention that, in one embodiment, more than one second polymer component may be used in a single blend with a first polymer component. Each of the second polymer component components is described above and the number of second polymer component in this embodiment is less than three and more preferably, two. In this embodiment of the invention the second polymer components differ in the alpha-olefin content with one being in the range of 5 wt % to 9 wt % alpha-olefin while the other is in the range of 10 wt % to 22 wt % alpha-olefin. The preferred alpha-olefin is ethylene. It is believed that the use of two second polymer component in conjunction with a single first polymer component leads to beneficial improvements in the tensile-elongation properties of the blends.

The Blend of First and Second Polymer Components

The copolymer blends of first polymer component and second polymer component of the instant invention may be prepared by any procedure that guarantees the intimate admixture of the components. For example, the components can be combined by melt pressing the components together on a Carver press to a thickness of about 0.5 millimeter (20 mils) and a temperature of about 180° C., rolling up the resulting slab, folding the ends together, and repeating the pressing, rolling, and folding operation about 10 times. Internal mixers are particularly useful for solution or melt blending. Blending at a temperature of about 180° C. to 240° C. in a Brabender Plastograph for about 1 to 20 minutes has been found satisfactory. Still another method that may be used for admixing the components involves blending the polymers in a Banbury internal mixer above the flux temperature of all of the components, e.g., 180° C. for about 5 minutes. The complete admixture of the polymeric components is indicated by the narrowing of the crystallization and melting transitions characteristic of the polypropylene crystallinity of the components to give a single or a small range crystallization and melting points for the blend. These batch mixing procedures are typically supplanted by continuous mixing processes in the industry. These processes are well known in the art and include single and twin screw mixing extruders, static mixers for mixing molten polymer streams of low viscosity, impingement mixers, as well as other machines and processes, designed to disperse the first polymer component and the second polymer component in intimate contact.

The polymer blends of the instant invention exhibit a remarkable combination of desirable physical properties. The incorporation of as little as 5% first polymer component in the propylene/alpha-olefin copolymers increases the propylene sequence melting point or the polymer softening point but, more significantly, reduces the range as compared to the propylene/alpha-olefin copolymer. In addition, the incorporation of first polymer component in accordance with the instant invention nearly eliminates the stickiness caused by the propylene/alpha-olefin copolymer. Further, the thermal characteristics of the copolymer blends are markedly improved over those of the second polymer component which is the propylene/alpha-olefin copolymers.

The crystallization temperature and the melting point of the blends are changed as a result of the blending operation. In an embodiment of the invention, the blend of first polymer component and second polymer component has single crystallization temperature and melting point. These temperatures are higher than the corresponding temperatures for the second polymer component and close to that of the first polymer component. In other embodiments, the second polymer component and the first polymer component have distinct melting and crystallization temperatures but have these temperatures closer together than would be expected for a combination of the second polymer component and the first polymer component. In all these cases the glass transition temperature of the second polymer component is retained in the polymer blend. This favorable combination of thermal properties permits their satisfactory use in injection molding operations without the orientation previously encountered. Injection molded articles prepared from the instant copolymer blends accordingly exhibit excellent long term dimensional stability. The advantages referred to above are obtained without the need of elaborate purification of the propylene/alpha-olefin copolymer or the tedious preparation of a carefully structured block copolymer. Further, by the use of the second polymer component and the first polymer component, a blend can be obtained with a lower glass transition temperature than would be expected for a random copolymer of the same composition as the blend. In particular, the glass transition temperature of the blend is closer to that of the second polymer component and lower than the glass transition temperature of the first polymer component. This can be accomplished without an exceptionally high alpha-olefin content in the polymer blend which we believe, while not meant to be limited thereby, would lead to degradation of the tensile-elongation properties of the blend.

The mechanism by which the desirable characteristics of the present copolymer blends are obtained is not fully understood. However, it is believed to involve a co-crystallization phenomenon between propylene sequences of similar stereoregularity in the various polymeric components, which results in one embodiment, a single crystallization temperature and a single melting temperature of the copolymer blend which is higher than those of the second polymer component which is the propylene/alpha-olefin component of the blend. In another embodiment, the combination of the first polymer component and the second polymer component has a melting point closer together than would be expected on a comparison of the properties of the individual components alone. It is surprising that in the one embodiment, the blend has a single crystallization temperature and a single melting temperature, since it would be expected by those skilled in the art that the blending of two crystalline polymers would result in a double crystallization temperature as well as a double melting temperature reflecting the two polymeric components. However, the intimate blending of the polymers having the required crystallinity characteristics apparently results in a crystallization phenomenon that modifies the other physical properties of the propylene/alpha-olefin copolymer, thus measurably increasing its commercial utility and range of applications.

While the above discussion has been limited to the description of the invention in relation to having only components one and two, as will be evident to those skilled in the art, the polymer blend compositions of the present invention may comprise other additives. Various additives may be present in the composition of the invention to enhance a specific property or may be present as a result of processing of the individual components. Additives which may be incorporated include, for example, fire retardants, antioxidants, plasticizers, and pigments. Other additives which may be employed to enhance properties include antiblocking agents, coloring agents, stabilizers, and oxidative-, thermal-, and ultraviolet-light-inhibitors. Lubricants, mold release agents, nucleating agents, reinforcements, and fillers (including granular, fibrous, or powder-like) may also be employed. Nucleating agents and fillers tend to improve rigidity of the article. The list described herein is not intended to be inclusive of all types of additives which may be employed with the present invention. Upon reading this disclosure, those of skill in the art will appreciate other additives may be employed to enhance properties of the composition. As is understood by the skilled in the art, the polymer blend compositions of the present invention may be modified to adjust the characteristics of the blend as desired.

As used herein, Mooney Viscosity was measured as ML (1+4) at 125° C. in Mooney units according to ASTM D1646.

The composition of Ethylene propylene copolymers, which are used as comparative examples, was measured as ethylene Wt % according to ASTM D 3900.

The composition of the second polymer component was measured as ethylene Wt % according to the following technique. A thin homogeneous film of the second polymer component, pressed at a temperature of about or greater than 150° C. was mounted on a Perkin Elmer PE 1760 infra red spectrophotometer. A full spectrum of the sample from 600 cm−1 to 400 cm−1 was recorded and the ethylene Wt % of the second polymer component was calculated according to Equation 1 as follows: ethylene Wt %=82.585−111.987X+30.045X ²

-   wherein X is the ratio of the peak height at 1155 cm⁻¹ and peak     height at either 722 cm⁻¹ or 732 cm⁻¹, which ever is higher.

Techniques for determining the molecular weight (Mn and Mw) and molecular weight distribution (MWD) are found in U.S. Pat. No. 4,540,753 (Cozewith, Ju and Verstrate) (which is incorporated by reference herein for purposes of U.S. practices) and references cited therein and in Macromolecules, 1998, volume 21, p 3360 (Verstrate et al) (which is herein incorporated by reference for purposes of U.S. practice) and references cited therein.

The procedure for Differential Scanning Calorimetry is described as follows. About 6 to 10 mg of a sheet of the polymer pressed at approximately 200° C. to 230° C. is removed with a punch die. This is annealed at room temperature for 80 to 100 hours. At the end of this period, the sample is placed in a Differential Scanning Calorimeter (Perkin Elmer 7 Series Thermal Analysis System) and cooled to about −50° C. to about −70° C. The sample is heated at 20° C./min to attain a final temperature of about 200° C. to about 220° C. The thermal output is recorded as the area under the melting peak of the sample which is typically peaked at about 30° C. to about 175° C. and occurs between the temperatures of about 0° C. and about 200° C. is measured in Joules as a measure of the heat of fusion. The melting point is recorded as the temperature of the greatest heat absorption within the range of melting of the sample. Under these conditions, the melting point of the second polymer component and the heat of fusion is lower than the first polymer component as outlined in the description above.

Composition distribution of the second polymer component was measured as described below. About 30 gms. of the second polymer component was cut into small cubes about ⅛″ on the side. This is introduced into a thick walled glass bottle closed with screw cap along with 50 mg of Irganox1076, an antioxidant commercially available from Ciba-Geigy Corporation. Then, 425 ml of hexane (a principal mixture of normal and iso isomers) is added to the contents of the bottle and the sealed bottle is maintained at about 23° C. for 24 hours. At the end of this period, the solution is decanted and the residue is treated with additional hexane for an additional 24 hours. At the end of this period, the two hexane solutions are combined and evaporated to yield a residue of the polymer soluble at 23° C. To the residue is added sufficient hexane to bring the volume to 425 ml and the bottle is maintained at about 31° C. for 24 hours in a covered circulating water bath. The soluble polymer is decanted and the additional amount of hexane is added for another 24 hours at about 31° C. prior to decanting. In this manner, fractions of the second polymer component soluble at 40° C., 48° C., 55° C. and 62° C. are obtained at temperature increases of approximately 8° C. between stages. Further, increases in temperature to 95° C. can be accommodated, if heptane, instead of hexane, is used as the solvent for all temperatures above about 60° C. The soluble polymers are dried, weighed and analyzed for composition, as wt % ethylene content, by the IR technique described above. Soluble fractions obtained in the adjacent temperature increases are the adjacent fractions in the specification above.

EPR in the data tables below is Vistalon 457, sold by the Exxon Chemical Company, Houston Tex.

The invention, while not meant to be limited thereby, is further illustrated by the following specific examples:

EXAMPLES Example 1 Ethylene/Propylene Copolymerization to Form the Second Polymer Component

Polymerizations were conducted in a 1 liter thermostatted continuous feed stirred tank reactor using hexane as the solvent. The polymerization reactor was full of liquid. The residence time in the reactor was typically 7–9 minutes and the pressure was maintained at 400 kpa. Hexane, ethene and propene were metered into a single stream and cooled before introduction into the bottom of the reactor. Solutions of all reactants and polymerization catalysts were introduced continuously into the reactor to initiate the exothermic polymerization. Temperature of the reactor was maintained at 41° C. by changing the temperature of the hexane feed and by circulating water in the external jacket. For a typical polymerization, the temperature of feed was about 0° C.

Ethene was introduced at the rate of 45 gms/min and propene was introduced at the rate of 480 gms/min. The polymerization catalyst, dimethyl silyl bridged bis-indenyl Hafnium dimethyl activated 1:1 molar ratio with N′, N′-Dimethyl anilinium-tetrakis(pentafluorophenyl)borate was introduced at the rate of 0.00897 gms/hr. A dilute solution of triisobutyl aluminum was introduced into the reactor as a scavenger of catalyst terminators: a rate of approximately 28.48 mol of scavenger per mole of catalyst was adequate for this polymerization. After five residence times of steady polymerization, a representative sample of the polymer produced in this polymerization was collected. The solution of the polymer was withdrawn from the top, and then steam distilled to isolate the polymer. The rate of formation of the polymer was 285.6 gms/hr. The polymer produced in this polymerization had an ethylene content of 13%, ML@125 (1+4) of 12.1 and had isotactic propylene sequences.

Variations in the composition of the polymer were obtained principally by changing the ratio of ethene to propene. Molecular weight of the polymer could be increased by a greater amount of ethene and propene compared to the amount of the polymerization catalyst. Dienes such as norbornene and vinyl norbornene could be incorporated into the polymer by adding them continuously during polymerization.

Example 2 Comparative Ethylene/Propylene Polymerization where the Propylene Residues are Atactic

Polymerizations were conducted in a 1 liter thermostatted continuous feed stirred tank reactor using hexane as the solvent. The polymerization reactor was full of liquid. The residence time in the reactor was typically 7–9 minutes and the pressure was maintained at 400 kpa. Hexane, ethene and propene were metered into a single stream and cooled before introduction into the bottom of the reactor. Solutions of all reactants and polymerization catalysts were introduced continuously into the reactor to initiate the exothermic polymerization. Temperature of the reactor was maintained at 45° C. by changing the temperature of the hexane feed and by using cooling water in the external reactor jacket. For a typical polymerization, the temperature of feed was about −10° C. Ethene was introduced at the rate of 45 gms/min and propene was introduced at the rate of 310 gms/min. The polymerization catalyst, dimethyl silyl bridged (tetramethylcyclopentadienyl) cyclododecylamido titanium dimethyl activated 1:1 molar ratio with N′,N′-Dimethyl anilinium-tetrakis(pentafluorophenyl)borate was introduced at the rate of 0.002780 gms/hr. A dilute solution of triisobutyl aluminum was introduced into the reactor as a scavenger of catalyst terminators: a rate of approximately 36.8 mole per mole of catalyst was adequate for this polymerization. After five residence times of steady polymerization, a representative sample of the polymer produced in this polymerization was collected. The solution of the polymer was withdrawn from the top, and then steam distilled to isolate the polymer. The rate of formation of the polymer was 258 gms/hr. The polymer produced in this polymerization had an ethylene content of 14.1 wt %, ML@125 (1+4) of 95.4.

Variations in the composition of the polymer were obtained principally by changing the ratio of ethene to propene. Molecular weight of the polymer could be increased by a greater amount of ethene and propene compared to the amount of the polymerization catalyst. These polymers are described as aePP in the Tables below.

Example 3 Analysis and Solubility of Several Second Polymer Components

In the manner described in Example 1 above, several second polymer components of the above specification were synthesized. These are described in the table below. Table 1 describes the results of the GPC, composition, ML and DSC analysis for the polymers.

TABLE 1 Ethylene Heat of ML (Mn) by (Mw) by wt % fusion Melting Point (1 + 4)@ SPC GPC GPC by IR J/g by DSC (° C.) 125° C. SPC-1 102000 248900 7.3 71.9 84.7 14 SPC-2 124700 265900 11.6 17.1 43.0 23.9 SPC-3 121900 318900 16.4 7.8 42.2 33.1 SPC-4 11.1 25.73 63.4 34.5 SPC-5 14.7 13.2 47.8 38.4 Comparative Polymers EPR 47.8 not not 40 detected detected aePP 11.7 not not 23 detected detected

Table 1: Analysis of the second polymer component and the comparative polymers

Table 2 describes the solubility of the second polymer component

TABLE 2 Wt. % soluble Wt. % soluble at Wt. % soluble Wt. % soluble at SPC 23° C. at 31° C. at 40° C. 48° C. SPC-1 1.0  2.9 28.3  68.5 SPC-2 6.5 95.7

SPC-3 51.6 52.3 2.6

SPC-4 18.7 83.6

SPC-5 36.5 64.2

ComparativePolymers

EPR 101.7

aePP 100.5

Table 2: Solubility of fractions of the second polymer component. Sum of the fractions add up to slightly more than 100 due to imperfect drying of the polymer fractions.

Table 3 describes the composition of the fractions of the second polymer component obtained in Table 2. Only fractions which have more than 4% of the total mass of the polymer have been analyzed for composition.

TABLE 3 Composition: Wt % ethylene in fraction soluble soluble soluble soluble soluble SPC at 23° C. at 31° C. at 40°C. at 48° C. at 56° C. SPC-1 8.0 7.6 SPC-2 12.0 11.2

SPC-3 16.8 16.5

SPC-4 13.2 11.2

SPC-5 14.9 14.6

Comparative

EPR 46.8

atactic ePP 11.8

Table 3: Composition of fractions of the second polymer component obtained in Table 2. The experimental inaccuracy in determination of the ethylene content is believed to about 0.4 wt % absolute.

Example 4

A total of 72 g of a mixture of the first polymer component and the second polymer component, as shown in the Table 4, column 2, were mixed in a Brabender intensive mixture for 3 minutes at a temperature controlled to be within 185° C. and 220° C. High shear roller blades were used for the mixing and approximately 0.4 g of Irganox-1076, an antioxidant available from the Novartis Corporation, was added to the blend. At the end of the mixing, the mixture was removed and pressed out into a 6″×6″ mold into a pad 025″ thick at 215° C. for 3 to 5 minutes. At the end of this period, the pad was cooled and removed and allowed to anneal for 3 to 5 days. Test specimens of the required dumbbell geometry were removed from this pad and evaluated on an Instron tester to produce the data shown in Table 4.

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was SPC-1 as characterized in Tables 1, 2 and 3 above.

TABLE 4 Composition in grams of FPC and SPC-1 FPC 64 56 48 40 32 24 16 8 0 SPC-1 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 4836 4243 3839 3274 2878 2475 2054 1705 1400 E = 25% 2782 3526 3460 3238 2863 2523 2146 1835 1502 E = 50% 2566 2539 2472 2589 2218 2135 1758 1501 1136 E = 100%

2509 2434 2231 2169 1907 1642 1376 1136 E = 150%

2239 2130 1844 1665 1407 1173 E = 200%

2247 2105 1854 1679 1440 1197 E = 250%

2245 2093 1887 1691 1478 1218 E = 300%

2253 2066 1896 1699 1474 1231 E = 350%

2251 2073 1905 1698 1476 1239 E = 400%

2251 2137 1879 1708 1478 1218 E = 450%

2247 2158 1869 1718 1474 1223 E = 500%

2246 2177 1901 1726 1470 1279 E = 550%

2229 2324 2350 2278 2261 E = 600%

3072 3229 3159 2970 E = 650%

3415 3538 3422 3010 E = 700%

3691 3135 E = 750%

3294

Table 4: Stress versus extension (E) data for blends of first polymer component and second polymer component where the second polymer component is Component SPC-1 in the tables above. Shaded areas represent broken samples. Clear areas represent lack of data due to extension beyond machine limits.

Example 5

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was Component SPC-2 as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 5 Composition in grams of FPC and SPC-2 FPC 64 56 48 40 32 24 16 8 0 SPC 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 4616 3477 2777 2221 1405 1012 705 488 326 E = 25% 2754 2863 2319 2178 1518 1143 822 634 472 E = 50%

2459 2221 1911 1517 1183 852 660 539 E = 100%

2243 1872 1522 1236 897 675 552 E = 150%

2261 1910 1546 1290 948 703 558 E = 200%

2271 1947 1581 1345 1003 737 574 E = 250%

2317 2037 1696 1486 1128 834 631 E = 300%

2341 2061 1788 1579 1210 904 690 E = 350%

2078 1919 1704 1313 995 778 E = 400%

2167 2096 1864 1452 1106 894 E = 450%

2221 2319 2069 1613 1239 1031 E = 500%

2397 2597 2344 1810 1398 1186 E = 550%

2976 2691 2060 1600 1350 E = 600%

3611 3224 2443 1854 1547 E = 650%

3660 2946 E = 700%

E = 750%

Table 5: Stress versus extension (E) data for blends of first polymer component and second polymer component where the second polymer component is component SPC-2 in the tables above. Shaded areas with no data represent broken samples. Clear areas represent lack of data due to extension beyond machine limits.

Example 6

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company. The second polymer component was Component SPC-3 as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 6 Composition in grams of FPC and SPC-3 FPC 64 56 48 40 32 24 16 8 0 SPC-3 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 3700 3333 2427 1574 770 421 161 89 70 E = 25% 2614 2989 2229 1607 840 498 224 135 99 E = 50%

2428 1944 1632 895 542 263 167 121 E = 100%

2399 1999 1644 945 575 281 180 131 E = 150%

2405 2043 1648 989 608 294 185 136 E = 200%

1995 1653 1069 675 329 188 135 E = 250%

1140 741 372 195 128 E = 300%

1195 807 423 209 124 E = 350%

1244 866 474 229 125 E = 400%

1273 925 528 255 129 E = 450%

979 580 285 136 E = 500%

1026 627 319 145 E = 550%

1081 676 354 154 E = 600%

1124 726 390 166 E = 650%

781 424 181 E = 700%

842 454 197 E = 750%

911 488 217 E = 800%

980 529 236 E = 850%

1049 577 256 E = 900%

1220 689 299 E = 950%

1322 760 322

Table 6: Stress versus extension (E) data for blends of first polymer component and second polymer component where the second polymer component is Component SPC-3 in the tables above. Shaded areas with no data represent broken samples. Clear areas represent lack of data due to extension beyond machine limits.

Example 7

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was Component SPC-4 as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 7 Composition in grams of FPC and SPC-4 FPC 64 56 48 40 32 24 16 8 0 SPC-4 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 4485 3719 2387 2387 1879 950 717 527 E = 25% 3983 3467 2944 2413 1960 1467 1082 893 686 E = 50% 2691 2473 2264 2186 1818 1429 1062 896 728 E = 100%

2448 2390 1951 1713 1387 1046 851 670 E = 150%

2496 2436 1965 1742 1390 1065 854 671 E = 200%

2523 2449 2001 1775 1411 1097 869 691 E = 250%

2532 2456 2038 1790 1448 1141 894 700 E = 300%

2537 2445 2070 1781 1496 1195 935 720 E = 350%

2548 2434 2087 1765 1568 1268 991 791 E = 400%

2564 2467 2152 1878 1682 1374 1089 877 E = 450%

2552

2242 1998 1854 1522 1235 1032 E = 500%

2407 2255 2101 1726 1416 1230 E = 550%

2642 2603 2398 1990 1637 1444 E = 600%

3048 3020 2689 2275 1882 1661 E = 650%

3410 2983 2540 2116 1824 E = 700%

3310 2730 2243 1821 E = 750%

3741 3183 2569 2387

Table 7: Stress versus extension (E) data for blends of first polymer component and second polymer component where the second polymer component is Component SPC-4 in the tables above. Shaded areas with no data represent broken samples. Clear areas represent lack of data due to extension beyond machine limits.

Example 8

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was a mixture of Component SPC-1 and Component SPC-5 as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 8 Composition in grams of FPC, SPC-1 and SPC-5 FPC 32 28 24 20 16 12 8 4 0 SPC-1 32 28 24 20 16 12 8 4 0 SPC-5 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 2158 1705 1382 875 523 342 215 149 97 E = 25% 2208 1903 1533 1035 656 437 296 216 141 E = 50% 1977 1823 1510 1102 725 489 342 257 174 E = 100% 1761 1655 1440 1154 798 546 379 286 200 E = 150% 1775 1585 1412 1194 868 605 417 304 211 E = 200% 1787 1582 1418 1236 942 669 465 329 219 E = 250% 1793 1601 1441 1280 1020 734 521 364 229 E = 300% 1802 1631 1475 1337 1103 801 585 410 245 E = 350% 1819 1662 1524 1409 1190 873 653 468 267 E = 400% 1841 1698 1592 1501 1290 955 729 530 297 E = 450% 1862 1740 1678 1626 1408 1058 813 606 337 E = 500% 1888 1757 1874 1791 1543 1187 920 697 387 E = 550% 1904 1930 2235 2027 1730 1352 1077 813 448 E = 600% 1935 2900 2627 2316 1988 1612 1335 998 521 E = 650% 1977 3452 2939 2659 2460 1978 1652 1233 616 E = 700% 2016

3159 3056 2530 2005 1492 759 E = 750%

3377 3857

2446 1836 914 E = 800%

1075 E = 850%

1277 E = 900%

Table 8: Stress versus extension (E) data for blends of first polymer component and EPR in the tables above. Shaded areas with no data represent broken samples.

Example 9 (Comparative)

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was Component EPR as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 9 Composition in grams of FPC and EPR FPC 64 56 48 40 32 24 16 8 0 EPR 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 3456 3125 2589 960 789 654 728 112 12 E = 25%

3358 3596 1122 999 890 754 244 18 E = 50%

1536 1356 1100 723 312 19 E = 100%

2125 1681 1292 812 432

E = 150%

1674 1330 860

E = 200%

1744 1391 898

E = 250%

Table 9: Stress versus extension (E) data for blends of first polymer component and EPR in the tables above. Shaded areas with no data represent broken samples.

Example 10 (Comparative)

The first polymer component was Escorene 4292, a commercially available homoisotactic polypropylene from Exxon Chemical Company, Houston, Tex. The second polymer component was aePP as characterized in Tables 1, 2 and 3 above. These components were mixed in the same manner as described for Example 4.

TABLE 10 Composition in grams of FPC and aePP FPC 64 56 48 40 32 24 16 8 0 aePP 8 16 24 32 40 48 56 64 72 Stress (psi) E = 10% 3258 3012 2258 872 635 558 432 189 15 E = 25% 2785 1687 975 870 856 215 15 E = 50% 1012 912 816 256 27 E = 100% 974 865 826 354 E = 150% 713 765 E = 200%

While the illustrative embodiments of the invention have been described with particularity, it will be understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the spirit and scope of the invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the examples and descriptions set forth herein but rather that the claims be construed as encompassing all the features of patentable novelty which reside in the present invention, including all features which would be treated as equivalents thereof by those skilled in the art to which the invention pertains. 

1. A polymer blend comprising: (a) polypropylene having at least about 90 wt % propylene-derived units; and (b) at least 44.4 wt % of a crystallizable polymer comprising propylene and from 7.3–16.4 wt % ethylene.
 2. A polymer blend according to claim 1 wherein the crystallizable polymer has a narrow molecular weight distribution.
 3. A polymer blend according to claim 1 wherein the crystallizable polymer has a MWD of from about 1.8 to about 5.0.
 4. A polymer blend according to claim 3 wherein the crystallizable polymer has a MWD of from about 2.0 to about 3.2.
 5. A polymer blend according to claim 1 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 6. A polymer blend according to claim 5 wherein the crystallizable polymer has a heat of fusion of from 7.8 to 71.8 J/g.
 7. A polymer blend according to claim 4 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 8. A polymer blend according to claim 1 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 9. A polymer blend according to claim 7 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 10. A polymer blend according to claim 1 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 11. A polymer blend according to claim 7 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 12. A polymer blend according to claim 1 wherein the crystallizable polymer has a Mn≧102000.
 13. A polymer blend according to claim 11 wherein the crystallizable polymer has a Mn≧102000.
 14. A polymer blend according to claim 1 wherein the crystallizable polymer has a Mw≧248900.
 15. A polymer blend according to claim 13 wherein the crystallizable polymer has a Mw≧248900.
 16. A polymer blend according to claim 1 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 17. A polymer blend according to claim 16 wherein the crystallizable polymer has a crystallinity of from about 5–40% of homoisotactic polypropylene.
 18. A polymer blend according to claim 15 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 19. A polymer blend according to claim 1 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 105° C.
 20. A polymer blend according to claim 18 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 105° C.
 21. A polymer blend according to claim 19 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 90° C.
 22. A polymer blend according to claim 20 wherein the crystallizable polymer has a melting point by DSC of from about 40 to about 90° C.
 23. A polymer blend according to claim 18 wherein the crystallizable polymer has a melting point by DSC of from about 40 to about 90° C.
 24. A polymer blend according to claim 1 wherein the blend comprises at least 55.55 wt % crystallizable polymer.
 25. A polymer blend according to claim 1 wherein the blend comprises from about 44.44 to about 88.88 wt % crystallizable polymer.
 26. A polymer blend according to claim 1 wherein the polypropylene has a melting point greater than 110° C.
 27. A polymer blend according to claim 26 wherein the polypropylene has a melting point greater than 130° C.
 28. A polymer blend according to claim 25 wherein the polypropylene has a melting point from about 115 to about 170° C.
 29. A polymer blend according to claim 23 wherein the polypropylene has a melting point from about 115 to about 170° C.
 30. A polymer blend according to claim 1 wherein the polypropylene is homopolymer, random copolymer, block copolymer or combination thereof.
 31. A polymer blend according to claim 30 wherein the polypropylene is a random copolymer containing up to 9 wt % comonomer.
 32. A polymer blend according to claim 31 wherein the comonomer is ethylene.
 33. A polymer blend according to claim 29 wherein the polypropylene is homopolymer, random copolymer, block copolymer or combination thereof.
 34. A polymer blend according to claim 33 wherein the polypropylene is a random copolymer containing up to 9 wt % comonomer.
 35. A polymer blend according to claim 1 wherein the crystallizable polymer is prepared in the presence of a bis (cyclopentadienyl) metal compound.
 36. A polymer blend according to claim 1 further comprising a non-conjugated diene.
 37. A polymer blend according to claim 7 wherein the glass transition temperature of the crystallizable polymer is retained in the blend.
 38. A polymer blend according to claim 1 wherein the blend further comprises a nucleating agent, a fire retardant, an antioxidant, a plasticizer, a pigment, an antiblocking agent, a coloring agent, a stabilizer, a lubricant, a mold release agent, a filler or a combination of more than one thereof.
 39. A polymer component for use in a polymer blend, the polymer component comprising: a crystallizable polymer comprising: (i) propylene; and (ii) from 7.3–16.4 wt % ethylene, wherein the polymer component has a weight average molecular weight (Mw) by GPC of at least 248,900 and a molecular weight distribution of from about 1.8 to about 5.0.
 40. A polymer component according to claim 39 wherein the crystallizable polymer has a MWD of from about 2.0 to about 3.2.
 41. A polymer component according to claim 39 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 42. A polymer component according to claim 41 wherein the crystallizable polymer has a heat of fusion of from 7.8 to 71.8 J/g.
 43. A polymer component according to claim 40 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 44. A polymer component according to claim 39 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 45. A polymer component according to claim 43 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 46. A polymer component according to claim 39 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 47. A polymer component according to claim 43 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 48. A polymer component according to claim 39 wherein the crystallizable polymer has a Mn≧102000.
 49. A polymer component according to claim 45 wherein the crystallizable polymer has a Mn≧102000.
 50. A polymer component according to claim 39 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 51. A polymer component according to claim 50 wherein the crystallizable polymer has a crystallinity of from about 5–40% of homoisotactic polypropylene.
 52. A polymer component according to claim 49 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 53. A polymer component according to claim 39 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 105° C.
 54. A polymer component according to claim 52 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 105° C.
 55. A polymer component according to claim 53 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 90° C.
 56. A polymer component according to claim 55 wherein the crystallizable polymer has a melting point by DSC of from about 40 to about 90° C.
 57. A polymer component according to claim 52 wherein the crystallizable polymer has a melting point by DSC of from about 40 to about 90° C.
 58. A polymer component according to claim 39 wherein the crystallizable polymer is prepared in the presence of a bis (cyclopentadienyl) metal compound.
 59. A polymer component for use in a polymer blend, the polymer component comprising: a crystallizable polymer comprising: (i) propylene; and (ii) from 7.3–16.4 wt % ethylene, wherein the polymer component has a weight average molecular weight (Mw) by GPC of at least 248,900 and a molecular weight distribution of from about 1.8 to about 5.0, and wherein when the polymer component is used in a polymer blend, the Tg of the crystallizable polymer is retained in the polymer blend.
 60. A polymer component according to claim 59 wherein the crystallizable polymer has a MWD of from about 2.0 to about 3.2.
 61. A polymer component according to claim 59 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 62. A polymer component according to claim 61 wherein the crystallizable polymer has a heat of fusion of from 7.8 to 71.8 J/g.
 63. A polymer component according to claim 60 wherein the crystallizable polymer has a heat of fusion<75 J/g.
 64. A polymer component according to claim 59 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 65. A polymer component according to claim 63 wherein the crystallizable polymer comprises crystallizable propylene sequences.
 66. A polymer component according to claim 59 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 67. A polymer component according to claim 65 wherein the crystallizable polymer has a ML (1+4) @ 125° C. of from 14–38.4.
 68. A polymer component according to claim 59 wherein the crystallizable polymer has a Mn≧102000.
 69. A polymer component according to claim 65 wherein the crystallizable polymer has a Mn≧102000.
 70. A polymer component according to claim 59 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 71. A polymer component according to claim 70 wherein the crystallizable polymer has a crystallinity of from about 5–40% of homoisotactic polypropylene.
 72. A polymer component according to claim 69 wherein the crystallizable polymer has a crystallinity of from about 2–65% of homoisotactic polypropylene.
 73. A polymer component according to claim 59 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 105° C.
 74. A polymer component according to claim 60 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 90° C.
 75. A polymer component according to claim 74 wherein the crystallizable polymer has a melting point by DSC of from about 40 to about 90° C.
 76. A polymer component according to claim 72 wherein the crystallizable polymer has a melting point by DSC of from about 25 to about 90° C.
 77. A polymer component according to claim 59 wherein the crystallizable polymer is prepared in the presence of a bis (cyclopentadienyl) metal compound.
 78. A polymer blend comprising: (a) a crystalline thermoplastic polymer; and (b) at least 44.4 wt % of a second polymer component comprising: (i) propylene and (ii) from 7.3–16.4 wt % ethylene, wherein the second polymer component polymer having a Mw≧about 248900, a Mn≧about 102000, a MWD of from about 1.8–5.0, a heat of fusion<75 J/g, a melting temperature of less than about 105° C., and a crystallinity of from about 2–65% of homoisotactic polypropylene. 